Vinyl Acetate content 18%
Melt mass flow rate 2.21
Suit for EVA foaming sole,shoes,sheet
Whatsapp :
+86 138-5857-5598
Product description
TL-V1803 is an ethylene/vinylene acetate copolymer. This product is manufactured by the high- ressure
process.By incorporating vinyl acetate (VA) into the ethylene chain, the high-pressure Process produces
co-polymerization on EVA
Typical Properties
Properties | Units | Test Method | Typical Value | Result |
Vinyl Acetate content | % | GB/T 30925-2014 | 17.0--20.5 | 19.2 |
Melt mass flow rate( 190C/2. 16kg) | g/ 10min | GB/T 3682. 1-2018 | 1.50--3.50 | 2.21 |
Appearance |
|
| ||
Chromomere | One per kg |
SH/T 1541-2019 | ≤ 10 | 4 |
Tailing grain | One per kg | ≤40 | 3 | |
Large and small grains | g/kg | Measured value | 1.6(0.0/ 1.6) | |
Flocculent | g/kg | ≤0. 1 | 0.0 | |
Density(23.0C) | g/cm3 | GB/T 1033. 1-2008 | Measured value | 0.938 |
Melting peak temperature | C | GB/T 19466.3-2004 | Measured value | 88 |
Application :
TL-V1803 is a general-purpose for X- linked foam shoes, mid- sole, EVA pipe, EVA sheet, EVA cable and wire ,
EVA gaskets. It provides good chemical resistance, excellent elasticity, and high flexible properties.
Vinyl Acetate content 18%
Melt mass flow rate 2.21
Suit for EVA foaming sole,shoes,sheet